Assessment of Thermal Aging of Aluminum Alloy by Acoustic Nonlinearity Measurement of Surface Acoustic Waves,

has now been assigned to an issue of Research in Nondestructive Evaluation, Issue 1


---


http://www.tandfonline.com/doi/full/10.1080/09349847.2016.1261213


Assessment of Thermal Aging of Aluminum Alloy by Acoustic Nonlinearity Measurement of Surface Acoustic Waves

Pages 1-15 | Accepted author version posted online: 20 Dec 2016, Published online: 20 Dec 2016

Acoustic nonlinearity measurements via contact and noncontact generations of surface acoustic waves (SAWs) were performed in order to characterize the thermal aging of aluminum alloy. The experiments were conducted on aluminum alloy samples (Al6061-T6) that were heat-treated at 220°C for different times (0 min, 20 min, 40 min, 1 h, 2 h, 10 h, 100 h, 1,000 h) and thus had the different levels of thermal aging. The acoustic nonlinearity of the specimens in two types of SAWs was observed according to the thermal aging. The fractional changes in the acoustic nonlinearity exhibited similar trends in both contact and noncontact SAWs, showing that the acoustic nonlinearity measurement via SAWs is independent of the SAW-excitation method. Furthermore, the fractional changes agreed well with the variation in the yield strength, which was a minimum when the acoustic nonlinearity reached its first peak. Then, the acoustic nonlinearity drastically dropped while the yield strength increased to its highest value. Thus, the variation in the acoustic nonlinearity can be perceived as an indicator of the aging level. These results demonstrate the potential feasibility of acoustic nonlinearity measurements via SAWs for the nondestructive evaluation of material degradations.


분류 제목 조회 수
International Nondestructive Evaluation of Thermal Aging in Al6061 Alloy by measuring Acoustic Nonlinearity of Laser-generated Surface Acoustic Waves     20964
International Stress estimation using the acoustoelastic effect of surface waves in weak anisotropic materials     21014
International Comparison of Linear and Nonlinear Ultrasonic Parameters in Characterizing Grain Size and Mechanical Properties of 304L Stainless Steel     20460
International Internal defect detection using laser-generated longitudinal waves in ablation regime     41151
International Synthetic aperture imaging of contact acoustic nonlinearity to visualize the closing interfaces using tone-burst ultrasonic waves     44163
International Dependence of Nonlinear Ultrasonic Characteristic on Second-Phase Precipitation in Heat-Treated Al 6061-T6 alloy     42796
International Relative Measurement of the Acoustic Nonlinearity Parameter using Laser Detection of an Ultrasonic Wave  fileimage   49930
International A Method to Estimate the Absolute Ultrasonic Nonlinearity Parameter from Relative Measurements  fileimage   53238
International Finite element analysis of a low-velocity impact test for glass fiber-reinforced polypropylene composites considering mixed-mode interlaminar fracture toughness  fileimage   51196
International Assessment of Thermal Degradation by Cumulative Variation of Ultrasonic Nonlinear Parameter     92473
International Assessment of Thermal Aging of Aluminum Alloys by Acoustic Nonlinearity Measurement of Surface Acoustic Waves     89220
International Absolute Measurement and Relative Measurement of Ultrasonic Nonlinear Parameter     87544
International Experimental Comparison of Nonlinear Parameters Obtained from Absolute Measurement and Relative Measurement     88693
International Comparison of Ultrasonic Nonlinear Parameters Measured by PZT and LiNbO3 Transducers     88953
International Nanotribological and wetting performance of hierarchical patterns     89657
International Demonstration of Disturbance Propagation and Amplification in Car-Following Situation for Enhancement of Vehicle Platoon System     91497
International Relative Measurement of Acoustic Nonlinear Parameters and Comparison of Sensitivity to Thermal Aging     90962
International Non-contact Measurement of Elastic Modulus by using Laser Ultrasonic     93899
International Relationship between Second- and Third-order Acoustic Nonlinear Parameters in Relative Measurement     89111
International Non-Contact Evaluation of Acoustic Nonlinearity of a Laser-Generated Surface Wave in a Plastically Deformed Aluminum Alloy     89231
Board Pagination ‹ Prev 1 2 3 4 5 Next ›
/ 5
Designed by hikaru100

나눔글꼴 설치 안내


이 PC에는 나눔글꼴이 설치되어 있지 않습니다.

이 사이트를 나눔글꼴로 보기 위해서는
나눔글꼴을 설치해야 합니다.

설치 취소

SketchBook5,스케치북5

SketchBook5,스케치북5

SketchBook5,스케치북5

SketchBook5,스케치북5

ISNDE Laboratory
203-2,Engineering Center Annex
Hanyang University,
222 Wangsimni-ro, Seongdong-gu
Seoul 04763, Korea
04763 서울특별시 성동구 왕십리로 222
한양대학교 공업센터 별관 203-2호
지능계측 및 비파괴평가 연구실
Tel: 02 - 2220 - 4220
Fax: 02 - 2299 - 7207