Assessment of Thermal Aging of Aluminum Alloy by Acoustic Nonlinearity Measurement of Surface Acoustic Waves,

has now been assigned to an issue of Research in Nondestructive Evaluation, Issue 1


---


http://www.tandfonline.com/doi/full/10.1080/09349847.2016.1261213


Assessment of Thermal Aging of Aluminum Alloy by Acoustic Nonlinearity Measurement of Surface Acoustic Waves

Pages 1-15 | Accepted author version posted online: 20 Dec 2016, Published online: 20 Dec 2016

Acoustic nonlinearity measurements via contact and noncontact generations of surface acoustic waves (SAWs) were performed in order to characterize the thermal aging of aluminum alloy. The experiments were conducted on aluminum alloy samples (Al6061-T6) that were heat-treated at 220°C for different times (0 min, 20 min, 40 min, 1 h, 2 h, 10 h, 100 h, 1,000 h) and thus had the different levels of thermal aging. The acoustic nonlinearity of the specimens in two types of SAWs was observed according to the thermal aging. The fractional changes in the acoustic nonlinearity exhibited similar trends in both contact and noncontact SAWs, showing that the acoustic nonlinearity measurement via SAWs is independent of the SAW-excitation method. Furthermore, the fractional changes agreed well with the variation in the yield strength, which was a minimum when the acoustic nonlinearity reached its first peak. Then, the acoustic nonlinearity drastically dropped while the yield strength increased to its highest value. Thus, the variation in the acoustic nonlinearity can be perceived as an indicator of the aging level. These results demonstrate the potential feasibility of acoustic nonlinearity measurements via SAWs for the nondestructive evaluation of material degradations.


분류 제목 조회 수
International Assessment of Thermal Degradation by Cumulative Variation of Ultrasonic Nonlinear Parameter     16562
International Assessment of Thermal Aging of Aluminum Alloys by Acoustic Nonlinearity Measurement of Surface Acoustic Waves     15835
International Absolute Measurement and Relative Measurement of Ultrasonic Nonlinear Parameter     16374
International Experimental Comparison of Nonlinear Parameters Obtained from Absolute Measurement and Relative Measurement     15281
International Comparison of Ultrasonic Nonlinear Parameters Measured by PZT and LiNbO3 Transducers     14891
International Nanotribological and wetting performance of hierarchical patterns     17055
International Demonstration of Disturbance Propagation and Amplification in Car-Following Situation for Enhancement of Vehicle Platoon System     17861
International Relative Measurement of Acoustic Nonlinear Parameters and Comparison of Sensitivity to Thermal Aging     17586
International Non-contact Measurement of Elastic Modulus by using Laser Ultrasonic     19534
International Relationship between Second- and Third-order Acoustic Nonlinear Parameters in Relative Measurement     17888
International Non-Contact Evaluation of Acoustic Nonlinearity of a Laser-Generated Surface Wave in a Plastically Deformed Aluminum Alloy     17056
International Influence of repetitive pulsed laser irradiation on the surface characteristics of an aluminum alloy in the melting regime     18170
International Real-time detection of surface cracks on silicon wafers during laser beam irradiation     18035
Domestic High power CW laser-induced damage of CMOS image sensor     18249
Domestic Measurement of Ultrasonic Nonlinear Parameter by Using Non-Contact Ultrasonic Receiver     18095
Domestic Study on the Nonlinear Electromagnetic Acoustic Resonance Method for the Evaluation of Hidden Damage in a Metallic Material     17859
International Influence of laser beam profiles on the frequency bandwidth of laser-generated surface acoustic waves     17842
International Laser ultrasonic inspection in ablation regime     17328
International Improvement of Crack Sizing Performance by using Nonlinear Ultrasonic Technique     18125
International In-Line Ultrasonic Monitoring for Sediments Stuck on Inner Wall of a Polyvinyl Chloride Pipe     25572
Board Pagination ‹ Prev 1 2 3 4 5 6 7 8 Next ›
/ 8
Designed by hikaru100

나눔글꼴 설치 안내


이 PC에는 나눔글꼴이 설치되어 있지 않습니다.

이 사이트를 나눔글꼴로 보기 위해서는
나눔글꼴을 설치해야 합니다.

설치 취소

SketchBook5,스케치북5

SketchBook5,스케치북5

SketchBook5,스케치북5

SketchBook5,스케치북5

ISNDE Laboratory
203-2,Engineering Center Annex
Hanyang University,
222 Wangsimni-ro, Seongdong-gu
Seoul 04763, Korea
04763 서울특별시 성동구 왕십리로 222
한양대학교 공업센터 별관 203-2호
지능계측 및 비파괴평가 연구실
Tel: 02 - 2220 - 4220
Fax: 02 - 2299 - 7207