Assessment of thermal degradation by cumulative variation of ultrasonic nonlinear parameter

  1. 1.
  2. 2.
Article

DOI: 10.1007/s12541-017-0003-x

Cite this article as:
Kim, J. & Jhang, KY. Int. J. Precis. Eng. Manuf. (2017) 18: 23. doi:10.1007/s12541-017-0003-x
  • 6Downloads

Abstract

The ultrasonic nonlinear parameter β has been studied for the evaluation of material degradation. However, there is a limit to the assessment of degradation induced by thermal aging in aluminum alloy because the nonlinear parameter may fluctuate with the aging time and thus it has not one-to-one correspondence with the thermal degradation. In order to overcome such limitation, we propose a cumulative nonlinear parameter βc defined by the accumulation of variation in the nonlinear parameter over the aging time. For verifying the usefulness of the proposed parameter, two kinds of aluminum alloy specimens heat-treated with different aging temperatures and aging times were tested. After the ultrasonic test has been completed, the tensile test was conducted for all specimens to measure the yield strength as a quantitative index of material degradation. Results showed that the nonlinear parameter β fluctuated in directions of both increase and decrease, while the strength decreased one-sidedly with the increase of aging time. On the other hand, the proposed parameter βc was one-sidedly increased, which showed strong exponential negative correlation with the yield strength. These tendencies were similar in different material and different aging temperature.


분류 제목 조회 수
International Assessment of Thermal Degradation by Cumulative Variation of Ultrasonic Nonlinear Parameter     31656
International Assessment of Thermal Aging of Aluminum Alloys by Acoustic Nonlinearity Measurement of Surface Acoustic Waves     29260
International Absolute Measurement and Relative Measurement of Ultrasonic Nonlinear Parameter     29955
International Experimental Comparison of Nonlinear Parameters Obtained from Absolute Measurement and Relative Measurement     28406
International Comparison of Ultrasonic Nonlinear Parameters Measured by PZT and LiNbO3 Transducers     29068
International Nanotribological and wetting performance of hierarchical patterns     30154
International Demonstration of Disturbance Propagation and Amplification in Car-Following Situation for Enhancement of Vehicle Platoon System     31852
International Relative Measurement of Acoustic Nonlinear Parameters and Comparison of Sensitivity to Thermal Aging     31493
International Non-contact Measurement of Elastic Modulus by using Laser Ultrasonic     33828
International Relationship between Second- and Third-order Acoustic Nonlinear Parameters in Relative Measurement     31013
International Non-Contact Evaluation of Acoustic Nonlinearity of a Laser-Generated Surface Wave in a Plastically Deformed Aluminum Alloy     30717
International Influence of repetitive pulsed laser irradiation on the surface characteristics of an aluminum alloy in the melting regime     31924
International Real-time detection of surface cracks on silicon wafers during laser beam irradiation     31218
Domestic High power CW laser-induced damage of CMOS image sensor     31726
Domestic Measurement of Ultrasonic Nonlinear Parameter by Using Non-Contact Ultrasonic Receiver     32478
Domestic Study on the Nonlinear Electromagnetic Acoustic Resonance Method for the Evaluation of Hidden Damage in a Metallic Material     31503
International Influence of laser beam profiles on the frequency bandwidth of laser-generated surface acoustic waves     32328
International Laser ultrasonic inspection in ablation regime     31252
International Improvement of Crack Sizing Performance by using Nonlinear Ultrasonic Technique     31464
International In-Line Ultrasonic Monitoring for Sediments Stuck on Inner Wall of a Polyvinyl Chloride Pipe     39001
Board Pagination ‹ Prev 1 2 3 4 5 6 7 8 Next ›
/ 8
Designed by hikaru100

나눔글꼴 설치 안내


이 PC에는 나눔글꼴이 설치되어 있지 않습니다.

이 사이트를 나눔글꼴로 보기 위해서는
나눔글꼴을 설치해야 합니다.

설치 취소

SketchBook5,스케치북5

SketchBook5,스케치북5

SketchBook5,스케치북5

SketchBook5,스케치북5

ISNDE Laboratory
203-2,Engineering Center Annex
Hanyang University,
222 Wangsimni-ro, Seongdong-gu
Seoul 04763, Korea
04763 서울특별시 성동구 왕십리로 222
한양대학교 공업센터 별관 203-2호
지능계측 및 비파괴평가 연구실
Tel: 02 - 2220 - 4220
Fax: 02 - 2299 - 7207