Assessment of Thermal Aging of Aluminum Alloy by Acoustic Nonlinearity Measurement of Surface Acoustic Waves,

has now been assigned to an issue of Research in Nondestructive Evaluation, Issue 1


---


http://www.tandfonline.com/doi/full/10.1080/09349847.2016.1261213


Assessment of Thermal Aging of Aluminum Alloy by Acoustic Nonlinearity Measurement of Surface Acoustic Waves

Pages 1-15 | Accepted author version posted online: 20 Dec 2016, Published online: 20 Dec 2016

Acoustic nonlinearity measurements via contact and noncontact generations of surface acoustic waves (SAWs) were performed in order to characterize the thermal aging of aluminum alloy. The experiments were conducted on aluminum alloy samples (Al6061-T6) that were heat-treated at 220°C for different times (0 min, 20 min, 40 min, 1 h, 2 h, 10 h, 100 h, 1,000 h) and thus had the different levels of thermal aging. The acoustic nonlinearity of the specimens in two types of SAWs was observed according to the thermal aging. The fractional changes in the acoustic nonlinearity exhibited similar trends in both contact and noncontact SAWs, showing that the acoustic nonlinearity measurement via SAWs is independent of the SAW-excitation method. Furthermore, the fractional changes agreed well with the variation in the yield strength, which was a minimum when the acoustic nonlinearity reached its first peak. Then, the acoustic nonlinearity drastically dropped while the yield strength increased to its highest value. Thus, the variation in the acoustic nonlinearity can be perceived as an indicator of the aging level. These results demonstrate the potential feasibility of acoustic nonlinearity measurements via SAWs for the nondestructive evaluation of material degradations.


Board Pagination ‹ Prev 1 2 3 4 5 6 7 8 9 Next ›
/ 9
Designed by hikaru100

나눔글꼴 설치 안내


이 PC에는 나눔글꼴이 설치되어 있지 않습니다.

이 사이트를 나눔글꼴로 보기 위해서는
나눔글꼴을 설치해야 합니다.

설치 취소

SketchBook5,스케치북5

SketchBook5,스케치북5

SketchBook5,스케치북5

SketchBook5,스케치북5

ISNDE Laboratory
203-2,Engineering Center Annex
Hanyang University,
222 Wangsimni-ro, Seongdong-gu
Seoul 04763, Korea
04763 서울특별시 성동구 왕십리로 222
한양대학교 공업센터 별관 203-2호
지능계측 및 비파괴평가 연구실
Tel: 02 - 2220 - 4220
Fax: 02 - 2299 - 7207