Slip damage of silicon wafers subjected to continuous infrared laser irradiation


Highlights

We investigate the laser irradiance inducing slip damage in a silicon wafer.

We develop a simulation model to predict the slip damage.

The model calculates the resolved shear stress and the temperature.

The slipping irradiance predicted by simulation agrees well with the experiments.


Abstract

Laser irradiation can cause damage to solids, such as slipping, cracking, melting, and ablation. Silicon crystals are brittle, so slipping is a serious problem because it can easily result in fracture. This study investigates the amount of continuous near-infrared (NIR) laser irradiance that induces slip damage in a single-crystal silicon wafer. For this purpose we developed a simulation model based on heat transfer and thermo-elastic analyses. To verify the simulation model, silicon wafer specimens were irradiated by a fiber laser beam (of wavelength 1065 nm), and the surface morphology after laser beam irradiation was inspected using optical microscopy (OM). The irradiation time was fixed at 10 s, and nine different irradiances from 180 W/cm2 to 380 W/cm2 were tested in steps of 25 W/cm2. No slip surface was found after exposure to the irradiances up to 230 W/cm2, but straight slips in the <110> direction appeared at the irradiances of 255 W/cm2 and above. These experimental findings agreed well with the simulation.

Keywords

  • Infrared laser
  • Silicon wafer
  • Thermal stress
  • Slip damage

분류 제목 조회 수
International Evaluation of yield strength by ultrasonic reconstruction of quadratic nonlinear Stress-Strain curve   65923
International Ultrasonic nonlinearity parameter in uniaxial stress condition   42891
International Applicability of nonlinear ultrasonic technique to evaluation of thermally aged CF8M cast stainless steel   6990
International Nondestructive Evaluation of Thermal Aging in Al6061 Alloy by measuring Acoustic Nonlinearity of Laser-generated Surface Acoustic Waves   66310
International Stress estimation using the acoustoelastic effect of surface waves in weak anisotropic materials   85890
International Comparison of Linear and Nonlinear Ultrasonic Parameters in Characterizing Grain Size and Mechanical Properties of 304L Stainless Steel   30996
International Internal defect detection using laser-generated longitudinal waves in ablation regime   108773
International Synthetic aperture imaging of contact acoustic nonlinearity to visualize the closing interfaces using tone-burst ultrasonic waves   87625
International Dependence of Nonlinear Ultrasonic Characteristic on Second-Phase Precipitation in Heat-Treated Al 6061-T6 alloy   74033
International Relative Measurement of the Acoustic Nonlinearity Parameter using Laser Detection of an Ultrasonic Wave  fileimage 100056
International A Method to Estimate the Absolute Ultrasonic Nonlinearity Parameter from Relative Measurements  fileimage 86767
International Finite element analysis of a low-velocity impact test for glass fiber-reinforced polypropylene composites considering mixed-mode interlaminar fracture toughness  fileimage 99076
International Assessment of Thermal Degradation by Cumulative Variation of Ultrasonic Nonlinear Parameter   207520
International Assessment of Thermal Aging of Aluminum Alloys by Acoustic Nonlinearity Measurement of Surface Acoustic Waves   124049
International Absolute Measurement and Relative Measurement of Ultrasonic Nonlinear Parameter   302769
International Experimental Comparison of Nonlinear Parameters Obtained from Absolute Measurement and Relative Measurement   167856
International Comparison of Ultrasonic Nonlinear Parameters Measured by PZT and LiNbO3 Transducers   140134
International Nanotribological and wetting performance of hierarchical patterns   123404
International Demonstration of Disturbance Propagation and Amplification in Car-Following Situation for Enhancement of Vehicle Platoon System   147464
International Relative Measurement of Acoustic Nonlinear Parameters and Comparison of Sensitivity to Thermal Aging   117490
Board Pagination ‹ Prev 1 2 3 4 5 6 Next ›
/ 6
Designed by hikaru100

나눔글꼴 설치 안내


이 PC에는 나눔글꼴이 설치되어 있지 않습니다.

이 사이트를 나눔글꼴로 보기 위해서는
나눔글꼴을 설치해야 합니다.

설치 취소

SketchBook5,스케치북5

SketchBook5,스케치북5

SketchBook5,스케치북5

SketchBook5,스케치북5

ISNDE Laboratory
203-2,Engineering Center Annex
Hanyang University,
222 Wangsimni-ro, Seongdong-gu
Seoul 04763, Korea
04763 서울특별시 성동구 왕십리로 222
한양대학교 공업센터 별관 203-2호
지능계측 및 비파괴평가 연구실
Tel: 02 - 2220 - 4220
Fax: 02 - 2299 - 7207