http://link.springer.com/article/10.1007/s12206-014-1206-z#page-1

 

Real-time detection of surface cracks on silicon wafers during laser beam irradiation

  • Sungho Choi
  • , Sung-Hee Yoon
  • , Kyung-Young Jhang 
  • , Wan-Soon Shin

Abstract

In this paper, a real-time in situ method to detect surface crack initiation on silicon wafers during laser beam irradiation is proposed. This method collects scattered light from the silicon wafer surface subjected to the laser irradiation. When the crack is initiated, the laser beam is strongly scattered by the crack so that the proposed method can monitor the time of crack initiation based on the increases of the level of the scattering signal. In order to demonstrate the performance of this method, a silicon wafer specimen was illuminated by a continuous wave (CW) fiber laser beam (wavelength of 1,070 nm) and the scattered light was detected at three different laser powers. The scattering signal showed a very high level at the time of crack initiation. The detected crack initiation times were 11.6 s, 5.5 s, and 2.5 s at irradiances of 130 W/cm2, 149 W/cm2, and 168 W/cm2, respectively. These results agree well with the theoretical predictions. Based on these results, we demonstrated that the proposed method is very effective for the real-time in situ detection of surface cracking induced by laser beam irradiation on silicon wafers.


분류 제목 조회 수
International Nanotribological and wetting performance of hierarchical patterns   123403
International Demonstration of Disturbance Propagation and Amplification in Car-Following Situation for Enhancement of Vehicle Platoon System   147462
International Relative Measurement of Acoustic Nonlinear Parameters and Comparison of Sensitivity to Thermal Aging   117490
International Non-contact Measurement of Elastic Modulus by using Laser Ultrasonic   231778
International Relationship between Second- and Third-order Acoustic Nonlinear Parameters in Relative Measurement  image 138433
International Non-Contact Evaluation of Acoustic Nonlinearity of a Laser-Generated Surface Wave in a Plastically Deformed Aluminum Alloy  image 159949
International Influence of repetitive pulsed laser irradiation on the surface characteristics of an aluminum alloy in the melting regime   279886
International Real-time detection of surface cracks on silicon wafers during laser beam irradiation   249344
Domestic High power CW laser-induced damage of CMOS image sensor   97753
Domestic Measurement of Ultrasonic Nonlinear Parameter by Using Non-Contact Ultrasonic Receiver   96816
Domestic Study on the Nonlinear Electromagnetic Acoustic Resonance Method for the Evaluation of Hidden Damage in a Metallic Material   95802
International Influence of laser beam profiles on the frequency bandwidth of laser-generated surface acoustic waves   121689
International Laser ultrasonic inspection in ablation regime   132339
International Improvement of Crack Sizing Performance by using Nonlinear Ultrasonic Technique   104057
International In-Line Ultrasonic Monitoring for Sediments Stuck on Inner Wall of a Polyvinyl Chloride Pipe   129216
International In situ detection of laser-induced slip initiation on the silicon wafer surface   104256
International Initiation time of near-infrared laser-induced slip on the surface of silicon wafers  image 112225
Domestic Evaluation of Ultrasonic Nonlinear Characteristics in Artificially Aged Al6061-T6   121811
Domestic Simulations for Internal Defect Inspection using Laser Generated Ultrasonic Wave in Ablation Regime   128079
International Slip damage of silicon wafers subjected to continuous infrared laser irradiation  image 105396
Board Pagination ‹ Prev 1 2 3 4 5 6 7 8 9 10 Next ›
/ 10
Designed by hikaru100

나눔글꼴 설치 안내


이 PC에는 나눔글꼴이 설치되어 있지 않습니다.

이 사이트를 나눔글꼴로 보기 위해서는
나눔글꼴을 설치해야 합니다.

설치 취소

SketchBook5,스케치북5

SketchBook5,스케치북5

SketchBook5,스케치북5

SketchBook5,스케치북5

ISNDE Laboratory
203-2,Engineering Center Annex
Hanyang University,
222 Wangsimni-ro, Seongdong-gu
Seoul 04763, Korea
04763 서울특별시 성동구 왕십리로 222
한양대학교 공업센터 별관 203-2호
지능계측 및 비파괴평가 연구실
Tel: 02 - 2220 - 4220
Fax: 02 - 2299 - 7207