http://www.sciencedirect.com/science/article/pii/S1567173914001072


Volume 14, Issue 6, June 2014, Pages 843–849

Cover image

Slip damage of silicon wafers subjected to continuous infrared laser irradiation


Highlights

We investigate the laser irradiance inducing slip damage in a silicon wafer.

We develop a simulation model to predict the slip damage.

The model calculates the resolved shear stress and the temperature.

The slipping irradiance predicted by simulation agrees well with the experiments.


Abstract

Laser irradiation can cause damage to solids, such as slipping, cracking, melting, and ablation. Silicon crystals are brittle, so slipping is a serious problem because it can easily result in fracture. This study investigates the amount of continuous near-infrared (NIR) laser irradiance that induces slip damage in a single-crystal silicon wafer. For this purpose we developed a simulation model based on heat transfer and thermo-elastic analyses. To verify the simulation model, silicon wafer specimens were irradiated by a fiber laser beam (of wavelength 1065 nm), and the surface morphology after laser beam irradiation was inspected using optical microscopy (OM). The irradiation time was fixed at 10 s, and nine different irradiances from 180 W/cm2 to 380 W/cm2 were tested in steps of 25 W/cm2. No slip surface was found after exposure to the irradiances up to 230 W/cm2, but straight slips in the <110> direction appeared at the irradiances of 255 W/cm2 and above. These experimental findings agreed well with the simulation.

Keywords

  • Infrared laser
  • Silicon wafer
  • Thermal stress
  • Slip damage

  1. Influence of laser beam profiles on the frequency bandwidth of laser-generated surface acoustic waves

    Date2015.09.16 CategoryInternational Views120461
    Read More
  2. Laser ultrasonic inspection in ablation regime

    Date2015.09.16 CategoryInternational Views129459
    Read More
  3. Improvement of Crack Sizing Performance by using Nonlinear Ultrasonic Technique

    Date2015.09.16 CategoryInternational Views103343
    Read More
  4. In-Line Ultrasonic Monitoring for Sediments Stuck on Inner Wall of a Polyvinyl Chloride Pipe

    Date2014.09.29 CategoryInternational Views128091
    Read More
  5. In situ detection of laser-induced slip initiation on the silicon wafer surface

    Date2014.09.29 CategoryInternational Views103733
    Read More
  6. Initiation time of near-infrared laser-induced slip on the surface of silicon wafers

    Date2014.09.29 CategoryInternational Views107444
    Read More
  7. Slip damage of silicon wafers subjected to continuous infrared laser irradiation

    Date2014.09.29 CategoryInternational Views104944
    Read More
  8. Thermal damages on the surface of a silicon wafer induced by a near-infrared laser

    Date2014.09.29 CategoryInternational Views609313
    Read More
  9. Crack Detection in Single-Crystalline Silicon Wafer Using Laser Generated Lamb Wave

    Date2014.03.05 CategoryInternational Views133710
    Read More
  10. Evaluation of Ultrasonic Nonlinear Characteristics in Heat-Treated Aluminum Alloy (Al-Mg-Si-Cu)

    Date2014.03.05 CategoryInternational Views188013
    Read More
  11. Application of Macrofiber Composite for Smart Transducer of Lamb Wave Inspection

    Date2014.03.05 CategoryInternational Views105800
    Read More
  12. Imaging of contact acoustic nonlinearity using synthetic aperture technique

    Date2014.03.05 CategoryInternational Views117443
    Read More
  13. Influence of slit width on harmonic generation in ultrasonic surface waves excited by masking a laser beam with a line arrayed slit

    Date2014.03.05 CategoryInternational Views125517
    Read More
  14. Acoustic Nonlinearity of a Laser-Generated Surface Wave in a Plastically Deformed Aluminum Alloy

    Date2014.03.05 CategoryInternational Views119743
    Read More
  15. Analysis of Transmitted Ultrasound signals through Apples at Different Storage Times using the Continuous Wavelet Transformation

    Date2014.03.05 CategoryInternational Views106318
    Read More
  16. Harmonic generation of an obliquely incident ultrasonic wave in solid-solid contact interfaces

    Date2014.03.05 CategoryInternational Views95149
    Read More
  17. NDE of low-velocity impact damages in composite laminates using ESPI, digital shearography and ultrasound C-scan techniques

    Date2014.03.05 CategoryInternational Views96145
    Read More
  18. Surface characteristics of aluminum 6061-T6 subjected to Nd:YAG pulsed-laser irradiation

    Date2012.06.21 CategoryInternational Views180718
    Read More
  19. Fatigue-induced microdamage characterization of stainless steel 316L using innovative nonlinear acoustics

    Date2012.06.21 CategoryInternational Views145122
    Read More
  20. Harmonic generation of an obliquely incident ultrasonic wave in solid-solid contact interfaces

    Date2012.06.21 CategoryInternational Views113005
    Read More
Board Pagination ‹ Prev 1 2 3 4 5 6 Next ›
/ 6
Designed by hikaru100

나눔글꼴 설치 안내


이 PC에는 나눔글꼴이 설치되어 있지 않습니다.

이 사이트를 나눔글꼴로 보기 위해서는
나눔글꼴을 설치해야 합니다.

설치 취소

SketchBook5,스케치북5

SketchBook5,스케치북5

SketchBook5,스케치북5

SketchBook5,스케치북5

ISNDE Laboratory
203-2,Engineering Center Annex
Hanyang University,
222 Wangsimni-ro, Seongdong-gu
Seoul 04763, Korea
04763 서울특별시 성동구 왕십리로 222
한양대학교 공업센터 별관 203-2호
지능계측 및 비파괴평가 연구실
Tel: 02 - 2220 - 4220
Fax: 02 - 2299 - 7207