In-Line Ultrasonic Monitoring for Sediments Stuck on Inner Wall of a Polyvinyl Chloride Pipe
http://www.hindawi.com/journals/tswj/2014/731621/
The Scientific World Journal
Volume 2014 (2014), Article ID 731621, 8 pages
http://dx.doi.org/10.1155/2014/731621
In-Line Ultrasonic Monitoring for Sediments Stuck on Inner Wall of a Polyvinyl Chloride Pipe
1Department of Mechanical Convergence Engineering, Hanyang University, Seoul 133-791, Republic of Korea
2School of Mechanical Engineering, Hanyang University, Seoul 133-791, Republic of Korea
Received 28 March 2014; Accepted 2 July 2014; Published 28 August 2014
Academic Editor: Ying Lei
Abstract
This research verified the applicability and effectiveness of the ultrasonic monitoring of sediments stuck on the inner wall of polyvinyl chloride (PVC) pipes. For identifying the transmittance of acoustic energy and the speed of sound in the PVC material, the pulse-echo ultrasonic testing was conducted for PVC sheets of different thicknesses. To simulate the solidified sediment, the hot melt adhesive (HMA) was covered on the inner wall of the PVC pipe in different heights. From the experiment, the speeds of sound in the PVC and the HMA materials were obtained as about 2258 and 2000 m/s, respectively. The thickness of the materials was calculated through the signal processing such as taking the absolute value and low pass filtering, the echo detection, and the measurement of the time of flight. The errors between actual and measured thicknesses of PVC sheets were below 5%. In the case of the substance stuck on the inner wall, the errors were below 2.5%. Since the pulse-echo ultrasonic inspection is available on the outer surface and its measurement accuracy was over 95%, it can be an efficient and effective in-service structural health monitoring for the sediment on the wall of PVC pipes.
-
Nanotribological and wetting performance of hierarchical patterns
-
Demonstration of Disturbance Propagation and Amplification in Car-Following Situation for Enhancement of Vehicle Platoon System
-
Relative Measurement of Acoustic Nonlinear Parameters and Comparison of Sensitivity to Thermal Aging
-
Non-contact Measurement of Elastic Modulus by using Laser Ultrasonic
-
Relationship between Second- and Third-order Acoustic Nonlinear Parameters in Relative Measurement
-
Non-Contact Evaluation of Acoustic Nonlinearity of a Laser-Generated Surface Wave in a Plastically Deformed Aluminum Alloy
-
Influence of repetitive pulsed laser irradiation on the surface characteristics of an aluminum alloy in the melting regime
-
Real-time detection of surface cracks on silicon wafers during laser beam irradiation
-
High power CW laser-induced damage of CMOS image sensor
-
Measurement of Ultrasonic Nonlinear Parameter by Using Non-Contact Ultrasonic Receiver
-
Study on the Nonlinear Electromagnetic Acoustic Resonance Method for the Evaluation of Hidden Damage in a Metallic Material
-
Influence of laser beam profiles on the frequency bandwidth of laser-generated surface acoustic waves
-
Laser ultrasonic inspection in ablation regime
-
Improvement of Crack Sizing Performance by using Nonlinear Ultrasonic Technique
-
In-Line Ultrasonic Monitoring for Sediments Stuck on Inner Wall of a Polyvinyl Chloride Pipe
-
In situ detection of laser-induced slip initiation on the silicon wafer surface
-
Initiation time of near-infrared laser-induced slip on the surface of silicon wafers
-
Evaluation of Ultrasonic Nonlinear Characteristics in Artificially Aged Al6061-T6
-
Simulations for Internal Defect Inspection using Laser Generated Ultrasonic Wave in Ablation Regime
-
Slip damage of silicon wafers subjected to continuous infrared laser irradiation