In situ detection of laser-induced slip initiation on the silicon wafer surface
http://www.ncbi.nlm.nih.gov/pubmed/25121706
In situ detection of laser-induced slip initiation on the silicon wafer surface.
Abstract
We propose a real-time in situ method to detect slip initiation on the surface of silicon wafers during high-power laser beam irradiation. In this method, light is collected from the surface of a silicon wafer subjected to laser irradiation. When the slip is initiated, it strongly scatters the laser beam, allowing detection of the time of the slip initiation based on the resulting sudden increase in the scattering signal. To demonstrate the performance of this method, a silicon wafer specimen was illuminated by a near-infrared continuous-wave fiber laser beam (of wavelength 1070 nm) at four different laser powers, and the scattered light was detected. The scattering signal increased suddenly at the time of slip initiation. To confirm the occurrence of slip, the surface morphologies of the silicon specimens after laser irradiation were analyzed using an optical microscope; surface slips were observed only in the specimens for which the sudden increase in scattering had been detected. Thus, the proposed method is shown to be very effective for the real-time in situ detection of surface slip initiation induced by high-power laser beam irradiation on silicon wafers.
-
Influence of slit width on harmonic generation in ultrasonic surface waves excited by masking a laser beam with a line arrayed slit
-
Evaluation of Ultrasonic Nonlinear Characteristics in Heat-Treated Aluminum Alloy
-
Initial Second Harmonic Generation in Narrowband Surface Waves by Multi-Line Laser Beams for Two Kinds of Spatial Energy Profile
-
Feasibility of MFC (Macro-Fiber Composite) Transducers for Guided Wave Technique
-
Imaging of contact acoustic nonlinearity using synthetic aperture technique
-
Thermal Damage Characterization of Silicon Wafer Subjected to CW Laser Beam
-
Application of Macrofiber Composite for Smart Transducer of Lamb Wave Inspection
-
Evaluation of Ultrasonic Nonlinear Characteristics in Heat-Treated Aluminum Alloy (Al-Mg-Si-Cu)
-
Crack Detection in Single-Crystalline Silicon Wafer Using Laser Generated Lamb Wave
-
A6061 합금의 석출경화 열처리에 따른 탄성파의 음향 특성 연구
-
Evaluation of Ultrasonic Nonlinear Characteristics in Heat-Treated Aluminum Alloy
-
Initial Second Harmonic Generation in Narrowband Surface Waves by Multi-Line Laser Beams for Two Kinds of Spatial Energy Profile Models
-
Feasibility of MFC (Macro-Fiber Composite) Transducers for Guided Wave Technique
-
Thermal damages on the surface of a silicon wafer induced by a near-infrared laser
-
Slip damage of silicon wafers subjected to continuous infrared laser irradiation
-
Simulations for Internal Defect Inspection using Laser Generated Ultrasonic Wave in Ablation Regime
-
Evaluation of Ultrasonic Nonlinear Characteristics in Artificially Aged Al6061-T6
-
Initiation time of near-infrared laser-induced slip on the surface of silicon wafers
-
In situ detection of laser-induced slip initiation on the silicon wafer surface
-
In-Line Ultrasonic Monitoring for Sediments Stuck on Inner Wall of a Polyvinyl Chloride Pipe