In situ detection of laser-induced slip initiation on the silicon wafer surface
http://www.ncbi.nlm.nih.gov/pubmed/25121706
In situ detection of laser-induced slip initiation on the silicon wafer surface.
Abstract
We propose a real-time in situ method to detect slip initiation on the surface of silicon wafers during high-power laser beam irradiation. In this method, light is collected from the surface of a silicon wafer subjected to laser irradiation. When the slip is initiated, it strongly scatters the laser beam, allowing detection of the time of the slip initiation based on the resulting sudden increase in the scattering signal. To demonstrate the performance of this method, a silicon wafer specimen was illuminated by a near-infrared continuous-wave fiber laser beam (of wavelength 1070 nm) at four different laser powers, and the scattered light was detected. The scattering signal increased suddenly at the time of slip initiation. To confirm the occurrence of slip, the surface morphologies of the silicon specimens after laser irradiation were analyzed using an optical microscope; surface slips were observed only in the specimens for which the sudden increase in scattering had been detected. Thus, the proposed method is shown to be very effective for the real-time in situ detection of surface slip initiation induced by high-power laser beam irradiation on silicon wafers.
-
Non-contact Measurement of Elastic Modulus by using Laser Ultrasonic
-
Relationship between Second- and Third-order Acoustic Nonlinear Parameters in Relative Measurement
-
Non-Contact Evaluation of Acoustic Nonlinearity of a Laser-Generated Surface Wave in a Plastically Deformed Aluminum Alloy
-
Influence of repetitive pulsed laser irradiation on the surface characteristics of an aluminum alloy in the melting regime
-
Real-time detection of surface cracks on silicon wafers during laser beam irradiation
-
Influence of laser beam profiles on the frequency bandwidth of laser-generated surface acoustic waves
-
Laser ultrasonic inspection in ablation regime
-
Improvement of Crack Sizing Performance by using Nonlinear Ultrasonic Technique
-
In-Line Ultrasonic Monitoring for Sediments Stuck on Inner Wall of a Polyvinyl Chloride Pipe
-
In situ detection of laser-induced slip initiation on the silicon wafer surface
-
Initiation time of near-infrared laser-induced slip on the surface of silicon wafers
-
Slip damage of silicon wafers subjected to continuous infrared laser irradiation
-
Thermal damages on the surface of a silicon wafer induced by a near-infrared laser
-
Crack Detection in Single-Crystalline Silicon Wafer Using Laser Generated Lamb Wave
-
Evaluation of Ultrasonic Nonlinear Characteristics in Heat-Treated Aluminum Alloy (Al-Mg-Si-Cu)
-
Application of Macrofiber Composite for Smart Transducer of Lamb Wave Inspection
-
Imaging of contact acoustic nonlinearity using synthetic aperture technique
-
Influence of slit width on harmonic generation in ultrasonic surface waves excited by masking a laser beam with a line arrayed slit
-
Acoustic Nonlinearity of a Laser-Generated Surface Wave in a Plastically Deformed Aluminum Alloy
-
Analysis of Transmitted Ultrasound signals through Apples at Different Storage Times using the Continuous Wavelet Transformation