Real-time detection of surface cracks on silicon wafers during laser beam irradiation
http://link.springer.com/article/10.1007/s12206-014-1206-z#page-1
Real-time detection of surface cracks on silicon wafers during laser beam irradiation
Abstract
In this paper, a real-time in situ method to detect surface crack initiation on silicon wafers during laser beam irradiation is proposed. This method collects scattered light from the silicon wafer surface subjected to the laser irradiation. When the crack is initiated, the laser beam is strongly scattered by the crack so that the proposed method can monitor the time of crack initiation based on the increases of the level of the scattering signal. In order to demonstrate the performance of this method, a silicon wafer specimen was illuminated by a continuous wave (CW) fiber laser beam (wavelength of 1,070 nm) and the scattered light was detected at three different laser powers. The scattering signal showed a very high level at the time of crack initiation. The detected crack initiation times were 11.6 s, 5.5 s, and 2.5 s at irradiances of 130 W/cm2, 149 W/cm2, and 168 W/cm2, respectively. These results agree well with the theoretical predictions. Based on these results, we demonstrated that the proposed method is very effective for the real-time in situ detection of surface cracking induced by laser beam irradiation on silicon wafers.
-
Non-contact Measurement of Elastic Modulus by using Laser Ultrasonic
-
Relationship between Second- and Third-order Acoustic Nonlinear Parameters in Relative Measurement
-
Non-Contact Evaluation of Acoustic Nonlinearity of a Laser-Generated Surface Wave in a Plastically Deformed Aluminum Alloy
-
Influence of repetitive pulsed laser irradiation on the surface characteristics of an aluminum alloy in the melting regime
-
Real-time detection of surface cracks on silicon wafers during laser beam irradiation
-
Influence of laser beam profiles on the frequency bandwidth of laser-generated surface acoustic waves
-
Laser ultrasonic inspection in ablation regime
-
Improvement of Crack Sizing Performance by using Nonlinear Ultrasonic Technique
-
In-Line Ultrasonic Monitoring for Sediments Stuck on Inner Wall of a Polyvinyl Chloride Pipe
-
In situ detection of laser-induced slip initiation on the silicon wafer surface
-
Initiation time of near-infrared laser-induced slip on the surface of silicon wafers
-
Slip damage of silicon wafers subjected to continuous infrared laser irradiation
-
Thermal damages on the surface of a silicon wafer induced by a near-infrared laser
-
Crack Detection in Single-Crystalline Silicon Wafer Using Laser Generated Lamb Wave
-
Evaluation of Ultrasonic Nonlinear Characteristics in Heat-Treated Aluminum Alloy (Al-Mg-Si-Cu)
-
Application of Macrofiber Composite for Smart Transducer of Lamb Wave Inspection
-
Imaging of contact acoustic nonlinearity using synthetic aperture technique
-
Influence of slit width on harmonic generation in ultrasonic surface waves excited by masking a laser beam with a line arrayed slit
-
Acoustic Nonlinearity of a Laser-Generated Surface Wave in a Plastically Deformed Aluminum Alloy
-
Analysis of Transmitted Ultrasound signals through Apples at Different Storage Times using the Continuous Wavelet Transformation