Slip damage of silicon wafers subjected to continuous infrared laser irradiation


Highlights

We investigate the laser irradiance inducing slip damage in a silicon wafer.

We develop a simulation model to predict the slip damage.

The model calculates the resolved shear stress and the temperature.

The slipping irradiance predicted by simulation agrees well with the experiments.


Abstract

Laser irradiation can cause damage to solids, such as slipping, cracking, melting, and ablation. Silicon crystals are brittle, so slipping is a serious problem because it can easily result in fracture. This study investigates the amount of continuous near-infrared (NIR) laser irradiance that induces slip damage in a single-crystal silicon wafer. For this purpose we developed a simulation model based on heat transfer and thermo-elastic analyses. To verify the simulation model, silicon wafer specimens were irradiated by a fiber laser beam (of wavelength 1065 nm), and the surface morphology after laser beam irradiation was inspected using optical microscopy (OM). The irradiation time was fixed at 10 s, and nine different irradiances from 180 W/cm2 to 380 W/cm2 were tested in steps of 25 W/cm2. No slip surface was found after exposure to the irradiances up to 230 W/cm2, but straight slips in the <110> direction appeared at the irradiances of 255 W/cm2 and above. These experimental findings agreed well with the simulation.

Keywords

  • Infrared laser
  • Silicon wafer
  • Thermal stress
  • Slip damage

Board Pagination ‹ Prev 1 2 3 Next ›
/ 3
Designed by hikaru100

나눔글꼴 설치 안내


이 PC에는 나눔글꼴이 설치되어 있지 않습니다.

이 사이트를 나눔글꼴로 보기 위해서는
나눔글꼴을 설치해야 합니다.

설치 취소

SketchBook5,스케치북5

SketchBook5,스케치북5

SketchBook5,스케치북5

SketchBook5,스케치북5

ISNDE Laboratory
203-2,Engineering Center Annex
Hanyang University,
222 Wangsimni-ro, Seongdong-gu
Seoul 04763, Korea
04763 서울특별시 성동구 왕십리로 222
한양대학교 공업센터 별관 203-2호
지능계측 및 비파괴평가 연구실
Tel: 02 - 2220 - 4220
Fax: 02 - 2299 - 7207