http://www.sciencedirect.com/science/article/pii/S1567173914001072


Volume 14, Issue 6, June 2014, Pages 843–849

Cover image

Slip damage of silicon wafers subjected to continuous infrared laser irradiation


Highlights

We investigate the laser irradiance inducing slip damage in a silicon wafer.

We develop a simulation model to predict the slip damage.

The model calculates the resolved shear stress and the temperature.

The slipping irradiance predicted by simulation agrees well with the experiments.


Abstract

Laser irradiation can cause damage to solids, such as slipping, cracking, melting, and ablation. Silicon crystals are brittle, so slipping is a serious problem because it can easily result in fracture. This study investigates the amount of continuous near-infrared (NIR) laser irradiance that induces slip damage in a single-crystal silicon wafer. For this purpose we developed a simulation model based on heat transfer and thermo-elastic analyses. To verify the simulation model, silicon wafer specimens were irradiated by a fiber laser beam (of wavelength 1065 nm), and the surface morphology after laser beam irradiation was inspected using optical microscopy (OM). The irradiation time was fixed at 10 s, and nine different irradiances from 180 W/cm2 to 380 W/cm2 were tested in steps of 25 W/cm2. No slip surface was found after exposure to the irradiances up to 230 W/cm2, but straight slips in the <110> direction appeared at the irradiances of 255 W/cm2 and above. These experimental findings agreed well with the simulation.

Keywords

  • Infrared laser
  • Silicon wafer
  • Thermal stress
  • Slip damage

  1. A noncontact NDE method using a laser generated focused-Lamb wave with enhanced defect-detection ability and spation resolution

    Date2012.05.03 CategoryInternational Views106746
    Read More
  2. "2.25Cr-1Mo강의 열화도 평가를 위한 비선형 음향효과 응용법"

    Date2012.05.03 CategoryDomestic Views106631
    Read More
  3. Nonlinear Ultrasonic Method to Detect Micro-delamination in Electronic Packaging

    Date2012.05.03 CategoryInternational Views106426
    Read More
  4. Application of Macrofiber Composite for Smart Transducer of Lamb Wave Inspection

    Date2014.03.05 CategoryInternational Views106251
    Read More
  5. Advanced Technologies for Estimation of Nonlinear Ultrasonic Parameter

    Date2012.05.03 CategoryInternational Views106238
    Read More
  6. Evaluation of material degrading using nonlinear acoustic effect

    Date2012.05.03 CategoryInternational Views105604
    Read More
  7. Slip damage of silicon wafers subjected to continuous infrared laser irradiation

    Date2014.09.29 CategoryInternational Views105410
    Read More
  8. 자동 초점 기법을 이용한 유리 내부 결함 검출

    Date2012.05.03 CategoryDomestic Views105344
    Read More
  9. Detection of Micro-Delamination in Electronic Packaging by Using the Ultrasonic Nonlinearity

    Date2012.05.03 CategoryInternational Views105187
    Read More
  10. Application of Nonlinear Ultrasonics to the NDE of Material Degradation

    Date2012.05.03 CategoryInternational Views105007
    Read More
  11. NONLINEAR BEHAVIOR OF ULTRASONIC WAVE AT CRACK

    Date2012.05.03 CategoryInternational Views104823
    Read More
  12. Estimation of Nonlinear Acoustic Parameter Using Bispectral Analysis

    Date2012.05.03 CategoryInternational Views104408
    Read More
  13. Thermal Damage Characterization of Silicon Wafer Subjected to CW Laser Beam

    Date2014.03.05 CategoryDomestic Views104328
    Read More
  14. In situ detection of laser-induced slip initiation on the silicon wafer surface

    Date2014.09.29 CategoryInternational Views104274
    Read More
  15. Research on the Nondestructive Measurement of Nonlinear Elastic Modulus by using Ultrasonic Wave

    Date2012.05.03 CategoryInternational Views104184
    Read More
  16. 비선형 응향효과에 의한 고온재료의 파괴인성 열화도 평가

    Date2012.05.03 CategoryDomestic Views104097
    Read More
  17. Improvement of Crack Sizing Performance by using Nonlinear Ultrasonic Technique

    Date2015.09.16 CategoryInternational Views104093
    Read More
  18. 레이저에 의한 집속형 램파의 집속도 향상을 위한 원호형 슬릿 설계

    Date2012.05.03 CategoryDomestic Views104074
    Read More
  19. SNR Improvement of AE Signal for Detection of Gas Leak from Tubes under Vibratory Environment

    Date2012.05.03 CategoryDomestic Views103112
    Read More
  20. Imaging of Defects in Thin Plate by Scanning of Laser-generated Focused-Lamb Waves

    Date2012.05.03 CategoryInternational Views103102
    Read More
Board Pagination ‹ Prev 1 2 3 4 5 6 7 8 9 10 Next ›
/ 10
Designed by hikaru100

나눔글꼴 설치 안내


이 PC에는 나눔글꼴이 설치되어 있지 않습니다.

이 사이트를 나눔글꼴로 보기 위해서는
나눔글꼴을 설치해야 합니다.

설치 취소

SketchBook5,스케치북5

SketchBook5,스케치북5

SketchBook5,스케치북5

SketchBook5,스케치북5

ISNDE Laboratory
203-2,Engineering Center Annex
Hanyang University,
222 Wangsimni-ro, Seongdong-gu
Seoul 04763, Korea
04763 서울특별시 성동구 왕십리로 222
한양대학교 공업센터 별관 203-2호
지능계측 및 비파괴평가 연구실
Tel: 02 - 2220 - 4220
Fax: 02 - 2299 - 7207